Growth Mechanism of TiB2 Powder Prepared by SHS-metallurgy

  • ZHANG Ting-An ,
  • DOU Zhi-He
Expand
  • School of Materials and Metallurgy, Northeastern University, Shenyang 110004, China

Received date: 2005-04-11

  Revised date: 2005-09-23

  Online published: 2006-05-20

Fold

摘要

采用自蔓延冶金法制备了TiB2微粉. 对相关的反应体系进行了DTA分析, 并采用XRD、扫描电镜以
及粒度分布技术对燃烧产物及浸出产物进行了分析和表征. 结果表明: Mg-B2O3-TiO2之间的反应为固-液-液-固反应机制; 燃烧产物主要有TiB2和MgO, 以及少量的Mg2TiO4和Mg3B2O6等相组成; 随着压样压力增加, TiB2颗粒变小, 添加MgO, TiB2颗粒亦减小, 添加TiB2, TiB2颗粒则明显
增大. 结合扫描电镜分析了燃烧产物的微观结构以及微观区域形成的原因, 确定了TiB2生长机制为一种在颗粒间生长, 另一种在颗粒内部形成.

关键词： 自蔓延高温合成; TiB2; 差热分析; 生长机理

本文引用格式

张廷安 , 豆志河 . 自蔓延冶金法制备 TiB2微粉的生长机理研究[J]. 无机材料学报, 2006 , 21(3) : 583 -590 . DOI: 10.3724/SP.J.1077.2006.00583

Abstract

TiB2 powder was prepared by SHS-metallurgy. The relative reaction systems were analyzed by DTA. The combustion products and leachable products were analyzed and characterized by XRD, SEM and granularity distribution. The results indicate that SHS reaction of Mg-TiO2-B2O3 system takes place through solid-liquid-liquid-solid reaction process. The combustion products consist of TiB2, MgO and a little Mg2TiO4 & Mg3B2O6. The TiB2 particles become thinner when the sample pressure increases; TiB2 particle becomes thinner when adding MgO to the reaction system and TiB2 particles become bigger when adding TiB2 to the reaction system. The microstructure of combustion products and the forming mechanism of the different micro-regions were analyzed by Micro-region-technology based on SEM. The growth mechanism of TiB2 can be determined that one is growing in particle-particle interfaces and the other is growing within particles.

Key words： TiB2; self-propagating high-temperature synthesis; DTA; growing mechanism

参考文献

1 张幸红.自蔓延高温合成TiC-Ni梯度功能材料研究. 哈尔滨: 哈尔滨工业大学出版社, 1993. 13-30.
2 傅正义, 袁润章, Muzir Z.A(FU Zheng-Yi, et al). 硅酸盐学报(Journal of the Chinese ceramic society), 1995, 23 (1): 27-32.
3 张廷安, 豆志河, 杨欢, 等. 东北大学学报(自然科学版), 2003, 24 (10): 936-939.
4 豆志河, 张廷安, 侯闯, 等. 中国有色金属学报, 2004, 14 (2): 322-326.
5 张廷安, 杨欢, 牛丽萍, 等. 中国有色金属学报, 2001, 11 (4): 567-570.
6 王延玲, 张廷安, 杨欢, 等. 稀有金属材料与工程, 2001, 30 (4): 310-313.
7 Merzhanov A,G. Self-propagating high-temperature synthesis. Twenty years of search and findings, ed. by Munir Z.A and Holt J.B, New York:VCH Publishers Inc, 1990. 1.
8 王为民, 傅正义, 金明姬(WANG Wei-Min, et al). 硅酸盐学报(Journal of the Chinese Ceramic Society), 1996, 24 (1): 53-57.
9 傅正义, 袁润章, Munir Z.A. 金属学报, 1993, 29 (7): 334.
10 Yuan R Z, Fu Z Y, Munir Z A, et al. J Mater Syn & Pro. 1993, 1 (3): 153-157.
11 Holt J B, Dunmead S D. Annual Review of Materials Science, 1991, 21: 305-334.
Options
文章导航

/

〈 〉