2007 , Vol. 22 >Issue 1: 53 - 58

DOI: https://doi.org/10.3724/SP.J.1077.2007.00053

研究论文

渗透水解 TiCl4制备纳米 TiO2

  • 陈云华 ,
  • 林安 ,
  • 甘复兴
展开
  • 武汉大学资源与环境科学学院, 武汉 430079

收稿日期: 2006-01-16

  修回日期: 2006-04-24

  网络出版日期: 2007-01-20

收起

Preparation of Nano-TiO2 by Dialysis Hydrolysis of TiCl4

  • CHEN Yun-Hua ,
  • LIN An ,
  • GAN Fu-Xing
Expand
  • College of Resource and Environmental Science of Wuhan University, Wuhan 430079, China

Received date: 2006-01-16

  Revised date: 2006-04-24

  Online published: 2007-01-20

Fold

摘要

利用渗透膜使TiCl4溶液中H+和Cl-慢慢渗透出来而水解得到凝胶, 然后用有机溶剂置换出其中的水分而干燥, 焙烧后即得纳米TiO2. 采用TEM、XRD、氮气吸脱附实验对样品进行了表征和分析. 所得产品颗粒细小、均匀, 比表面积大. 晶体相转变温度高, 700℃焙烧仍然为锐态矿型晶体, 900℃转变为金红石型晶体. 文中还将该法和加热水解法、氨水沉淀法以及钛酸丁酯溶胶-凝胶法进行了比较.

关键词： 凝胶; 纳米; TiO2; 制备

本文引用格式

陈云华 , 林安 , 甘复兴 . 渗透水解 TiCl4制备纳米 TiO2[J]. 无机材料学报, 2007 , 22(1) : 53 -58 . DOI: 10.3724/SP.J.1077.2007.00053

Abstract

A dialysis membrane was used to make H+ and Cl- dialyze out slowly during the hydrolysis of TiCl4, and then TiO2 gel was obtained. The gel was dried by different methods and then calcined. The samples were characterized by transmission electron microscope (TEM), X-ray diffraction (XRD), BET surface area and BJH pore size distribution. For comparison, the hydrolysis of TiCl4 by the methods of heating and adding ammonia, and the hydrolysis of tetrabutyl titanate by the sol-gel method were researched. The product prepared by the dialysis method has an enormous specific surface area and the crystallites are small and uniform. It has a high phase transform temperature, keeping anatase after calcination at 700℃ and transforming into rutile phase at 900℃.

Key words： gel; nanometer; TiO2; preparation

参考文献

[1] 高濂, 陈锦元, 黄军华, 等(GAO Lian, {et al).
无机材料学报(Journal of Inorganic Materials), 1995, 10 (4): 423--427.
[2] Souhir Boujday, et al. Solar Energy Materials & Solar Cells, 2004, 83: 421--433.
[3] Hu Z S, et al. Powder Technology, 1999, 101: 205--210.
[4]赵文宽, 方佑龄, 张开诚, 等(ZHAO Wen-Kuan, {et al). 无机材料学报(Journal of Inorganic Materials), 1998, 13 (4): 608--612.
[5] 曹爱红, 等. 硅酸盐学报(Journal of the Chinese Ceramic Society), 2002, 增刊: 83--86.
[6] 黄晖, 等. 硅酸盐通报(Journal of the Chinese Ceramic Society), 2000, (4): 8--12.
[7] Zeng Tingying, et al. Materials Chemistry and Physics, 1998, 56: 163--170.
[8] 施利毅, 等. 华东理工大学学报, 1998, 24 (3): 291--297.
[9] 张青红, 高濂, 郭景坤, 等(ZHANG Qing-Hong, {et al).
无机材料学报(Journal of Inorganic Materials), 2000, 15 (6): 992--998.
[10] 陈洪龄, 王延儒, 时钧, 等(CHEN Hong-Ling, {et al).
无机材料学报(Journal of Inorganic Materials), 2002, 17 (1): 149--153.
[11] 刘宝春, 等, 南京化工大学学报, 1997, 19 (4): 76--79.
[12] 李燕, 等. 安徽建筑工业学院学报, 1997, 5 (3): 54--56.
[13] Yang Shaofeng, et al. Materials Chemistry and Physics, 2002, 77: 501--506.
[14] 李国华, 等. 硅酸盐学报(Journal of the Chinese Ceramic Society), 2003, 31 (3): 272--277.
[15] Gopal M, et al. J. Mater. Sci., 1997, 32: 6001--6008.

Options
文章导航

/

〈 〉