Preparation and Characteristic of One-dimensional Magnesium Borate Nanomaterials

Expand
  • (College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024, China)

Received date: 2010-01-11

  Revised date: 2010-03-05

  Online published: 2010-08-25

摘要

采用了溶剂热法(水和乙醇做溶剂)合成出了物相和形貌可控的一维硼酸镁纳米棒. 研究结果表明, 在溶剂的超临界状态下, 无需表面活性剂的参与, 能直接合成出一维硼酸镁纳米棒. 通过对不同反应阶段生成产物的XRD结构分析, 表明Mg2B2O5结构的形成经历了从Mg(OH)2到MgBO2(OH)的转变; 通过对相应阶段生成产物的SEM观察, 表明Mg2B2O5纳米棒的形貌经历了从片状到短柱状再到棒状的演变. 分析认为Mg2B2O5纳米棒的形成遵循着形核→溶解→各向异性生长→再结晶的过程.

本文引用格式

李天保, 梁 建, 许并社, 王 进 . 硼酸镁一维纳米材料的制备和表征[J]. 无机材料学报, 2010 , 25(9) : 947 -951 . DOI: 10.3724/SP.J.1077.2010.00947

Abstract

Single-crystalline magnesium borate nanorods were fabricated by solvothermal method at the supercritical conditions. This reaction condition enabled the formation of magnesium borate with one dimensional nanostructure without the involvement of surfactants. The microstructures of as-synthesized products prepared at different reaction stages were characterized by X-ray diffraction. The results show that Mg2B2O5 structure is obtained through an intermediate transition from Mg(OH)2 to MgBO2(OH), and then from MgBO2(OH) to Mg2B2O5. The morphology of the products at corresponding stages were observed by scanning electron microscope(SEM), showing that the formation process of Mg2B2O5 nanorods was from flake-like to short columnar and then to rod. The result suggests that the formation of Mg2B2O5 nanorods follow a process from nucleation → dissolution → anisotropic growing → recrystallization.

参考文献

[1]Peng L M, Zhu S J, Ma Z Y, et al. High temperature creep deformation of Al18B4O33 whisker-reinforced 8009 Al composite.Mater. Sci. Eng. A,1999, 265(1/2):63-70
[2]Shahare D L, Dhoble S J, Moharil S V. Preparation and characterization of magnesium-borate phosphor.J. Mater. Sci. Lett,1993, 12(23):1873-1874
[3]Wu P L, Tian Z, Wang L D, et al. Effect of changing rate of residual stress on thermal expansion behavior of magnesium borate whisker-reinforced aluminum composite.Thermochim. Acta,2007, 455(1/2):7-10
[4]Kuchibhatla S V N T, Karakoti A S, Bera D, et al. One dimensional nanostructured materials.Prog. Mater. Sci,2007, 52(5):699-913
[5]Xia Y, Yang P, Sun Y, et al. One-dimensional nanostructures: synthesis, characterization, and applications.Adv. Mater,2003, 15(5):353-389
[6]Ma R, Bando Y, Sato T. Nanowires of metal borates.Appl. Phys. Lett,2002, 81(18):3467-3469
[7]Li Y, Fan Z, Lu J G, et al. Synthesis of magnesium borate (Mg2B2O5) nanowires by chemical vapor deposition method.Chem. Mater,2004, 16 (13):2512-2514
[8]Ma R, Bando, Y, Golberg D, et al. Nanotubes of magnesium borate.Angew. Chem. Int. Ed,2003, 42(16):1836-1838
[9]Elssfah E M, Elsanousi H A, Zhang J, et al. Synthesis of magnesium borate nanorods.Mater. Lett,2007, 61(22):4358-4361
[10]Zhang J, Li Z, Zhang B. Formation and structure of single crystalline magnesium borate (Mg3B2O6) nanobelts.Mater. Chem. Phys,2006, 98(2/3):195-197
[11]Rao C N R, Deepak F L, Gundiah G, et al. Inorganic nanowires.Prog. Solid State Chem,2003, 31(1/2):5-147
[12]Lu J G, Chang P, Fan Z. Quasi-one-dimensional metal oxide materials- synthesis, properties and applications.Mater. Sci. Eng. R,2006, 52(1/2/3):49-91
[13]Rabenau A. The role hydrothermal synthesis in preparative chemistry.Angew. Chem. Int. Ed. Engl,1985, 24(12):1026-1040

文章导航

/