用碳酸氢铵作为沉淀剂,将硝酸镥、硝酸铝和硝酸铈配成混合溶液,采用反滴定共沉淀及低温煅烧前驱体的方法制备 Lu3Al5O12(Ce)纳米发光粉体.采用热分析(TG-DTA)、傅立叶红外光谱(FTIR)、X射线衍射(XRD)、透射电镜(TEM)和光致发光(PL)等分析测试方法对Lu3Al5O12(Ce)粉体制备过程中的物理化学变化及粉体的激发发射发光性能进行了研究.结果表明,采用反滴定共沉淀法制备工艺,经过1000℃煅烧2h,可以得到晶粒尺寸为30nm左右,仅有轻微团聚,单一石榴石相的Lu3Al5O12(Ce)粉体.并且在1000℃处理得到的粉体的光致发光最强.
Ce3+-doped Lutetium aluminum garnet Lu3Al5O12 phosphors were prepared by an anti co-precipitation from mixing solution of lutetium, aluminum and cerium nitrates using the ammonium hydrogen carbonate as precipitate,followed by the calcination at low temperatures. TG-DTA, FTIR, XRD, TEM and Photoluminescence were used to characterize the as-prepared phosphors. The calcining temperature has distinctly influence on the particle size and the photoluminescence of the prepared Lu3Al5O12(Ce) powders. The resulted Lu3Al5O12(Ce) powder calcined at 1000℃ for 2h has an average particle size of 30nm. And its photoluminescence is the strongest among the powders calcined in the range from 850℃ to 1200℃.
[1]van Eijk C W E. Nucl. Instr. Meth. A , 1997,392(2): 285-290.
[2]Lempicki A, Randles M H, Wisniew ski D, et al. IEEE Trans. Nucl. Sci., 1995, 429(4): 280-284.
[3]van Eijk C W E, Andriessen J, Dorenbos P, et al., Nucl. Instr. Meth. A, 1994, 348(2-3): 546-550.
[4]Nikl M, Mihokova E, Mares J A, et al. Phys. Stat. Sol. (a), 2000,181: R10-R12.
[5]Ogino H, Yoshikawa A, Lee J H, et al. J. Cryst. Growth, 2003, 253(3): 314-318.
[6]Yoshikawa A, Nikl M, Ogino H, et al. J. Cryst.Growth, 2003,250(1): 94-99.
[7]Yoshikawa A, Ogino H, Lee J H, et al. Opt. Mater.,2003, 24(2): 275-279.
[8]Manalert R, Rahaman M N. J. Mater. Sci.,1996,31(13): 3453-3458. [9]Tachiwaki T, Yoshinaka M, Hirota K, et al. Solid State Comm., 2001, 119(11):603-606.
[10]Kinsman K M, Mckittrick J, Sluzky E, et al. J. Am. Ceram. Soc., 1994,77(11): 2866-2872.
[11]Li J G, Ikegami T, Lee J H, et al. J. Eur. Ceram. Soc., 2000, 20(14): 2395-2405.
[12]Vrolijk J W G A, Metselaar R. Homogeneous coprecipitation of precursor for preparation of yttrium aluminum garnet, in: P. Vincenzini (Ed.), Ceramics Today - Tomorrow’s Ceramics, Elsevier Science Publishers, Amsterdam, 1991: 935-941.
[13]Pillai K T, Kamat R V, Vaigya V N, et al. Mater. Chem. Phys., 1996, 44(3): 255-260.
[14]Shea L E, Mckittrick J, Lopez O A, et al. J. Am. Ceram. Soc., 1996, 79(12): 3257-3265.
[15]Hayashi K, Toyoda S, Takebe H, et al. J. Ceram. Soc. Jpn., 1991, 99(7): 550-555.
[16]Dean J A. LANGE’s Handbook of Chemistry(兰氏化学手册),第15版. [17]杭州大学化学系分析化学教研室.分析化学手册(第二分册)分析化学,第二版. 北京:化学工业出版社,1997.
[18]Jiang D Y , Wang Z L, Zhang F L, et al. J.Mater.Res., 1998, 13(10): 2950-2955.