用共烧法制备了以(SrCo0.8Fe0.2O3-δ)0.85(SrSnO3)0.15 (SCF-SS)多孔层为支撑体和SrCo0.8Fe0.2O3-δ(SCF) 致密层为顶层膜的管状非对称透氧陶瓷膜; 并对其相组成、微形貌以及氧分离性能进行了表征. 研究发现: SCF和SCF-SS之间有较好的兼容性; 当共烧温度为1150℃时, 获得的非对称陶瓷膜的致密层厚度为50μm, 支撑体的显气孔率为19.3%; 900和800℃时, 非对称膜样品(壁厚1.4mm, 外径10.3mm, 长度为4.1cm)的氧渗透率分别为1.91和1.01mL·cm-2·min-1, 分别比同样几何尺寸的SCF对称膜样品高24%和36%.
The tubular asymmetric membrane (TAM) was prepared by co-firing method with dense top layer of SrCo0.8Fe0.2O3-δ(SCF) and porous substrate layer of (SrCo0.8Fe0.2O3-δ)0.85(SrSnO3)0.15 (SCF-SS). Its phase composition, morphology and oxygen permeability were investigated. The results show that SCF layer and SCF-SS layer have desirable compatibility for configuration of asymmetric membrane. The resulting TAM sample sintered at 1150℃ has the dense layer of SCF with thickness of 50μm and the SCF-SS substrate with apparent porosity of 19.3%. The permeation rates of the resulting TAM are 1.91mL·cm-2·min-1 at 900℃ and 1.01mL·cm-2·min-1 at 800℃, respectively, which are 24% and 36% higher than those of the SCF tubular symmetric membrane (TSM) with same size(wall thickness of 1.4mm, outer diameter of 10.3mm, and length of 4.1cm).
[1] Bouwmeester H J M, Burgraaf A J. Fundamentals of Inorganic Membrane Science and Technology, Elsevier, New York, 1996, 451-461.
[2] 邵宗平, 熊国兴, 杨惟慎, 等(SHAO Zong-Ping, et al). 无机材料学报(Journal of Inorganic Materials), 2001, 16 (2): 297-304.
[3] Steele B C H. J. Power Sources, 1994, 49 (1-3): 1-14.
[4] Teraoka Y, Zhang H M, Furukawa S, et al. Chem. Lett., 1985, 167 (11): 1743-1746.
[5] Fan C G, Deng Z Q, Zuo Y B, et al. Solid State Ionics, 2004, 166 (3-4): 339-342.
[6] Buchler O, Serra J M, Meulenber W A, et al. Solid State Ionics, 2007, 178 (1-2): 91-99.
[7] Li K, Tan X Y, Liu Y T. J. Membr. Sci., 2006, 272 (1-2): 1-5.
[8] Jin W Q, Li S G, Huang P, et al. J. Membr. Sci., 2001, 185 (2): 237-243.
[9] Fan C G, Zuo Y B, Lu J Q, et al. Key Eng. Mater., 2007, 334-335: 921-924.
[10] Lee T H, Yang Y L, Jacobson A J, et al. Solid State Ionics, 1997, 100 (1-2): 77-85.