Ca0.3(Li1/2Sm1/2)0.7TiO3微波介质陶瓷的低温烧结研究

  • 李月明1 ,
  • 宋婷婷1 ,
  • 尤源2 ,
  • 胡元云2 ,
  • 刘维良1 ,
  • 唐春宝1
展开
  • 1. 景德镇陶瓷学院, 景德镇 333001; 2. 浙江正原电气股份有限公司, 嘉兴 314003

收稿日期: 2008-02-27

  修回日期: 2008-04-25

  网络出版日期: 2008-11-20

收起

Research on Low-temperature Sintering of Ca0.3(Li1/2Sm1/2)0.7TiO3 Microwave Dielectric Ceramics

  • LI Yue-Ming ,
  • SONG Ting-Ting ,
  • YOU Yuan ,
  • HU Yuan-Yun ,
  • LIU Wei-Liang ,
  • TANG Chun-Bao
Expand
  • 1. Jingdezhen Ceramic Institute, Jingdezhen 333001, China; 2. Zhejiang Zhenyuan Electric Co. Ltd., Jiaxing 314003, China

Received date: 2008-02-27

  Revised date: 2008-04-25

  Online published: 2008-11-20

Fold

摘要

采用传统陶瓷制备工艺, 制备了掺杂Na2O-CaO-B2O3(NCB)氧化物的Ca0.3(Li1/2Sm1/2)0.7TiO3(CLST)陶瓷, 研究了NCB掺杂量与晶相组成、显微结构、烧结性能及微波介电性能的关系. 研究结果表明: 复合氧化物NCB掺杂量在1wt%～15wt%范围内没有杂相生成, 晶相仍呈斜方钙钛矿结构. 随着NCB添加量的增加, 陶瓷致密化温度和饱和体积密度降低, 介电常数εr、无载品质因数与谐振频率乘积Qf值也呈下降趋势, 频率温度系数τf向正方向增大. NCB氧化物掺杂能有效地将CLST陶瓷的烧结温度由1300℃降低至900℃. 添加12.5wt% NCB的CLST陶瓷在低温900℃烧结5h仍具有良好的微波介电性能: εr=73.7, Qf=1583GHz, τf=140.1×10-6/℃, 满足高介多层微波器件的设计要求.

关键词： Ca0.3(Li1/2Sm1/2)0.7TiO3; Na2O-CaO-B2O3; 低温烧结; 微波介质陶瓷

本文引用格式

李月明1 , 宋婷婷1 , 尤源2 , 胡元云2 , 刘维良1 , 唐春宝1 . Ca0.3(Li1/2Sm1/2)0.7TiO3微波介质陶瓷的低温烧结研究[J]. 无机材料学报, 2008 , 23(6) : 1293 -1297 . DOI: 10.3724/SP.J.1077.2008.01293

Abstract

The NCB(Na2O-CaO-B2O3)-doped Ca0.3(Li1/2Sm1/2)0.7TiO3(CLST) ceramics were fabricated via the traditional ceramic process. The relation between NCB dopant contents and the crystal structure, microstructure, sintering behavior, and dielectric properties of CLST ceramics were investigated systematically. The results indicate that the second phases are not found when NCB dopant contents are in the range from 1wt% to 15wt% and the major phase of CLST ceramics is still orthorhombic perovskite. With the increase of NCB content, the densification temperature and bulk density of CLST ceramics decrease, the dielectric constant εr and the product of quality factor and resonance frequency Qf value also decrease, and the temperature coefficient of resonant frequency τf increases to positive. NCB can effectively decrease the sintering temperature of CLST from 1300℃ to 900℃. The sample of CLST with 12.5wt% NCB sintered at 900℃ for 5h still has excellent dielectric properties: εr=73.7, Qf=1583GHz, τf=140.1×10-6/℃, which satisfies the design demand of high dielectric constant and multilayer microwave components.

Key words： Ca0.3(Li1/2Sm1/2)0.7TiO3; Na2O-CaO-B2O3; low-temperature sintering; microwave

参考文献

[1] 赵梅瑜, 王依琳. 电子元件与材料, 2002, 21 (2): 30-34.
[2] 童建喜, 张启龙, 杨辉, 等. 硅酸盐学报, 2006, 34 (11): 1135-1140.
[3] Hong Zheng, Ian M Reaney, Duncan Muir, et al. J. Eur. Ceram. Soc., 2007, 27 (16): 4479-4487.
[4] Dernovsek O, Naeini A, Preu G, et al. J. Eur. Ceram. Soc., 2001, 21 (10-11): 1693-1697.
[5] Cho Kyung-Hoon, Lim Jong-Bong, Nahm Sahn, et al. J. Eur. Ceram. Soc., 2007, 27 (2-3): 1053-1058.
[6] Albina Y Borisevich, Peter K Davies. J. Am. Ceram. Soc., 2004, 87 (6): 1047-1052.
[7] 张启龙, 杨辉, 刘兴元, 等. 硅酸盐学报, 2005, 33 (7): 793-798.
[8] 管恩祥, 陈玮, 罗澜(GUAN En-Xiang, et al). 无机材料学报(Journal of Inorganic Materials), 2007, 22 (2): 315-318.
[9] 李月明, 宋婷婷, 胡元云, 等(LI Yue-Ming, et al). 无机材料学报(Journal of Inorganic Materials), 2008, 23 (4): 695-699.
[10] Shannon R D. Acta Cryst., 1976, A32: 751-767.
[11] 黄静. 武汉: 华中科技大学博士学位论文, 2004.
[12] 张迎春. 铌钽酸盐微波介质陶瓷材料. 北京: 科学出版社, 2006. 3-7.
[13] 何进, 杨传仁. 电子元件与材料, 1995, 14 (2): 7-13.
Options
文章导航

/

〈 〉