研究论文

基体诱导法制备碳纳米管/云母复合导电粉

  • 彭 珂 ,
  • 张庆堂 ,
  • 陈国强 ,
  • 周固民 ,
  • 林浩强 ,
  • 瞿美臻
展开
  • (1. 中国科学院 成都有机化学研究所, 成都 610041; 2. 中国科学院研究生院, 北京 100049)

收稿日期: 2006-11-12

  修回日期: 2006-12-15

  网络出版日期: 2007-11-20

Carbon Nanotube/Mica Composite Powder Prepared by Substrate-induced Method

  • PENG Ke ,
  • ZHANG Qing-Tang ,
  • CHEN Guo-Qiang ,
  • ZHOU Gu-Min ,
  • LIN Hao-Qiang ,
  • QU Mei-Zhen1
Expand
  • (1. Chengdu Organic Chemical Institute of Chinese Academy of Sciences, Chengdu 610041, China; 2. Graduate University of the Chinese Academy Sciences, Beijing 100049, China)

Received date: 2006-11-12

  Revised date: 2006-12-15

  Online published: 2007-11-20

摘要

基体诱导法制备碳纳米管(CNT)/云母复合导电粉, 即用聚乙烯醇(PVA)或聚丙烯酰胺(PAM)对云母进行处理, 将处理后的云母与CNT分散液混合, 使CNT吸附在云母表面. 测试复合导电粉的体积电阻率(ρ)发现, CNT含量为1.0wt%时, CNT/云母的ρ为2.0×104Ω·cm, 而用PVA修饰的云母制备CNT/云母, 体积电阻率达到86.6Ω·cm. 运用XPS、SEM对复合导电粉进行表征. 结果表明当云母表面经PVA修饰后, 能改善CNT在其表面的吸附和分散, 使CNT/云母的体积电阻率明显降低.


本文引用格式

彭 珂 , 张庆堂 , 陈国强 , 周固民 , 林浩强 , 瞿美臻 . 基体诱导法制备碳纳米管/云母复合导电粉[J]. 无机材料学报, 2007 , 22(6) : 1131 -1134 . DOI: 10.3724/SP.J.1077.2007.01131

Abstract

Carbon nanotube (CNT)/Mica conductice composite powder was prepared by a substrate-induced method. The mica was modified by poly (vinyl alcohol) (PVA) or polyacrylamide (PAM), and mixed with CNT suspension, then CNT adsorbed on mica surface. The resistivity (ρ) of composite powder was measured. XPS, SEM were used to characterize the obtained CNT/Mica. The results show that the resistivity is 2.0×104 Ω·cm when the unmodified mica is used to prepare 1.0wt% CNT/Mica, while the resistivity can reach 86.6Ω·cm when modified mica is used. Modified mica can improve CNT adsorption and dispersion, and decrease the resistivity of CNT/Mica remarkably.

参考文献

[1] Sun J, Gao L, Jin X H. Ceram. Inter., 2005, 31 (6): 893--896.
[2] 张幸红, 洪长青, 韩杰才, 等(ZHANG Xing-Hong, et al). 无机材料学报(Journal of Inorganic Materials), 2006, 21 (4): 899--905.
[3] Zou Y B, Feng Y C, Wang L, et al. Carbon, 2004, 42 (2): 271--277.
[4] An L N, Xu W X, Wang C M, et al. Adv. Mater., 2004, 16 (22): 2036--2040.
[5] Han S-C, Song M-S, Lee H, et al. J. Electrochem. Soc., 2003, 150: A889--893.
[6] Li X L, Kang F Y, Shen W C. Carbon, 2006, 44 (7): 1334--1336.
[7] Sandler J, Shaffer M S P, Prasse T, et al. Polymer, 1999, 40 (21): 5967--5971.
[8] Fan J H, Wan M X, Zhu D B, et al. Synth. Metal., 1999, 102: 1266--1267.
[9] Rul S, Peigney A, Capria E, et al. Acta Mater., 2004, 52 (4): 1061--1067.
[10] Agrawal S, Kumar A, Frederick M J, et al. Small, 2005, 1: 823--826.
文章导航

/