采用阳极氧化法制备铈掺杂TiO2/Ti光电极, 用SEM、XRD、XRF、XPS和UV/VIS/NIR对光电极的性能进行表征, 并对其可见光照射下的光电催化性能进行了测试. 研究结果表明:在成膜电压为160V, 电流密度为100mA/cm2, Ce(NO3)3浓度为960mg/L条件下制备的铈掺杂TiO2/Ti光电极在降解罗丹明B的实验中表现出良好的光电催化活性.
Cerium-doped TiO2/Ti photoelectrodes were prepared by anodization. The photoelectrodes were characterized by SEM, XRD, XRF, XPS and UV/VIS/NIR, and their photoelectrocatalytic performance under visible light irradiation was also investigated. Taking degradation efficiency of rhodamine B as indication, the preparing conditions of Cerium-doped TiO2/Ti photoelectrodes were optimized. The optimal parameters are voltage of 160V, current density of 100mA/c 2 and Ce(NO3)3 concentration of 960 mg/L.
[1] Fujishima A, Honda K. Nature, 1972, 238: 37--38.
[2] Li X Z, Liu H L, Yue P T. Environ. Sci. Technol., 2000, 34 (11): 4401--4406.
[3] Tokudome H, Miyauchi M. Chem. Lett., 2004, 33 (9): 1108--1109.
[4] 杨松旺, 高濂(YANG Song-Wang, et al). 无机材料学报(Journal of Inorganic Materials), 2005, 20 (4): 785--788.
[5] Sato S, Nakamura R, Abe S. Appl. Cataly. Gen., 2005, 284 (1-2): 131--137. [6] Kuroda Y, Mori T, Yagi K, et al. Langmuir, 2005, 21 (17): 8026--8034.
[7] Li D, Haneda H, Hishita S, et al. Res. Chem. Int., 2005, 31 (4-6): 331--341. [8] Wang Z P, Jun X, Cai W M, et al. J. Environ. Sci., 2005, 17 (1): 76--80.
[9] Noguchi D, Kawamata Y, Nagatomo T. J. Electrochem. Soc., 2005, 152 (9): D124--D129.
[10] 刘红艳, 高濂(LIU Hong-Yan, et al). 无机材料学报(Journal of Inorganic Materials), 2005, 20 (2): 470--474.
[11] 高濂, 郑珊, 张青红. 纳米氧化钛光催化材料及应用, 化学工业出版社, 2002. 39--45.
[12] 陈崧哲, 张彭义, 祝万鹏, 等. 化学进展, 2004, 16 (4): 613--619.