B₂O₃/MCM-41的制备和结构表征

李正平; 高濂

中国科学院上海硅酸盐研究所高性能陶瓷和超微结构国家重点实验室上海 200050

收稿日期:2002-12-16 修回日期:2003-03-14 出版日期:2004-01-20 网络出版日期:2004-01-20

Preparation and Structural Characterization of B₂O₃/MCM-41 Material

LI Zheng-Ping; GAO Lian

State Key Lab of High Performance Ceramics and Superfine Microstructure; Shanghai Institute of Ceramics; Chinese Academy of Sciences; Shanghai 200050; China

Received:2002-12-16 Revised:2003-03-14 Published:2004-01-20 Online:2004-01-20

摘要/Abstract

摘要： 以硼酸三丁酯为硼源,用溶液液相移植的方法制备了B₂O₃/MCM-41材料.用DTA、 XRD、FTIR、XPS和氮气吸附-脱附曲线等手段表征了合成的材料.结果表明:硼物种发生析晶,以B₂O₃的形式存在,硼的配位状态为三配位的BO₃结构单元.

关键词: B₂O₃, MCM-41, 液相移植

Abstract: The B₂O₃/MCM-41 material was prepared by the solution-grafting method, using tri-butyl borate as boron source. DTA, XRD, FTIR, XPS and N₂ adsorption-desorption isotherms were employed to characterize the synthesized materials. The results show that boron specie separates out and exists as cubic B₂O₃ after calcining at 400℃. The trigonal BO₃ is as the basic coordinated unit in B₂O₃/MCM-41. The solution-grafting and following calcination have little effect on the structure of MCM-41 host.

Key words: B₂O₃, MCM-41, solution-grafting

中图分类号:

TB383

李正平,高濂. B₂O₃/MCM-41的制备和结构表征[J]. 无机材料学报.

LI Zheng-Ping,GAO Lian. Preparation and Structural Characterization of B₂O₃/MCM-41 Material[J]. Journal of Inorganic Materials.

参考文献

[1] Kresge C T, Leonowicz M E, Roth W J, et al. Nature, 1992, 359: 710--712.
[2] Beck J S, Vartuli J C, Roth W J, et al. J. Am. Chem. Soc., 1992, 114: 10834--10843.
[3] Moller K, Bein T. Chem. Mater., 1998, 10: 2950--2963.
[4] Ying J Y, Mehnert C P, Wong M S. Agnew. Chem. Int. Ed., 1999, 38: 56--77.
[5] Stein A, Melde B J, Schroden R C. Adv. Mater., 2000, 12: 1403--1419.
[6] Liu Z, Sakamoto Y, Ohsuna T, et al. Angew. Chem. Int. Ed., 2000, 39: 3107--3110.
[7] Han Y-J, Kim J M, Stucky G D. Chem. Mater., 2000 12: 2068--2069.
[8] Hirai T, Okubo H, Komasawa I. J. Phys. Chem. B, 1999, 103: 4228--4230.
[9] Zhang Z, Dai S, Fan X, et al. J. Phys. Chem. B, 2001, 105: 6755--6758.
[10] Agger J R, Anderson M W, Pemble M E, et al. J. Phys. Chem. B, 1998, 102: 3345--3353.
[11] Abe T, Tachibana Y, Uemastsu T, et al. J. Chem. Soc., Chem. Commun., 1995. 1617--1618.
[12] Aronson B J, Blanford C F, Stein A. Chem. Mater., 1997, 9: 2842--2851.
[13] Zheng S, Gao L, Zhang Q, et al. J. Mater. Chem., 2000, 10: 723--727.
[14] Dumeignil F, Guelton M, Rigole M, et al. Colloids and Surfaces A, 1999, 158: 75--81.
[15] 徐柏庆, 程时标(XU Bai-Qing et al). 物理化学学报(Acta Phys.-Chim. Sin.), 2001, 17 (5): 443--447.
[16] Sayari A, Moudrakovski I, Danumsh C, et al. J. Phys. Chem., 1995, 99: 16373--16379.
[17] Trong On D, Joshi P N, Kaliaguine S. J. Phys. Chem., 1996, 100: 6743--6748.
[18] 李正平, 高濂, 郑珊(LI Zheng-Ping, et al). 无机材料学报(Journal of Inorganic Materials), 2002, 17 (4): 759--764.
[19] Li Z, Gao L, Zheng S. Appl. Catal. A, 2002, 236: 163--171.
[20] Wagner C D, Riggs W M, Davis L E, et al. Handbook of X-ray photoelectron spectroscopy. Minnesota: Perkin-Elmer, Eden Prairie. 1979. 36--37.

B₂O₃/MCM-41的制备和结构表征

Preparation and Structural Characterization of B₂O₃/MCM-41 Material

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	黄长兴, 崔骏, 裴元生. B₂O₃-SiO₂-Na₂O缓释材料的合成工艺参数优化及其缓释机理[J]. 无机材料学报, 2019, 34(6): 653-659.
[2]	强小虎,李彬彬,黄大建,周松毅. 氧化硼对聚磷酸钙纤维力学和降解性能的影响[J]. 无机材料学报, 2019, 34(2): 201-206.
[3]	姚晓刚, 任海深, 姜少虎, 张奕, 顾忠元, 林慧兴. CaO-B₂O₃玻璃助烧的零膨胀系数β-锂霞石陶瓷的制备及性能研究[J]. 无机材料学报, 2018, 33(4): 385-389.
[4]	王觅堂, 方龙, 李梅, 柳召刚, 胡艳宏, 张晓伟. 稀土掺杂对ZnO-B₂O₃-SiO₂玻璃热稳定性及结构的影响[J]. 无机材料学报, 2017, 32(6): 643-648.
[5]	李裕, 米琴, 薛泽慧. 磁性MCM-41分离回收RT培司废水中四甲基氢氧化铵的研究[J]. 无机材料学报, 2016, 31(7): 694-698.
[6]	李圭, 钟玲, 袁霞, 吴剑, 罗和安. Sn掺杂MCM-41介孔分子筛的制备、表征及催化性能研究[J]. 无机材料学报, 2010, 25(10): 1041-1046.
[7]	李月明1,宋婷婷1,尤源2,胡元云2,刘维良1,唐春宝1. Ca_0.3(Li_1/2Sm_1/2)_0.7TiO₃微波介质陶瓷的低温烧结研究[J]. 无机材料学报, 2008, 23(6): 1293-1297.
[8]	刘彩华,王雯娟,程文萍,于心玉,杨建国,何鸣元. 含稳定骨架铁的Fe-MCM-41介孔分子筛的合成与表征[J]. 无机材料学报, 2008, 23(1): 171-174.
[9]	张文丽,金建国,张晓丽. Na₂O-B₂O₃-SiO₂-SnO₂系统的分相与析晶[J]. 无机材料学报, 2005, 20(1): 205-209.
[10]	张存满,徐政,万克树,刘茜. 高氮含量的有序氮氧化物介孔材料的研究[J]. 无机材料学报, 2004, 19(3): 559-565.
[11]	胡冰,施剑林,陈航榕. 镧系金属掺杂MCM-41分子筛的合成与表征[J]. 无机材料学报, 2004, 19(2): 329-334.
[12]	祝柏林,谢长生,曾大文,胡木林,胡军辉. ZnO-Sb₂O₃烧结体系的电导和气敏性能[J]. 无机材料学报, 2004, 19(2): 313-318.
[13]	戴能利,杨建虎,戴世勋,胡丽丽,张德宝. Yb³⁺掺杂SiO₂-Bi₂O₃-B₂O₃玻璃的物理性质及光谱性质[J]. 无机材料学报, 2003, 18(4): 744-750.
[14]	刘见芬,蒋引珊,王安平,宋波. 蒙脱石原位合成高热稳定性Al-MCM-41[J]. 无机材料学报, 2003, 18(4): 867-871.
[15]	张存满,徐政,刘茜,万克树. 气氛对Al-MCM-41热稳定性的影响[J]. 无机材料学报, 2003, 18(4): 861-866.