混合导电体Y1-xLaxBa2Cu3O7-δ透氧膜的透氧性能研究

无机材料学报

混合导电体Y_1-xLa_xBa₂Cu₃O_7-δ透氧膜的透氧性能研究

宋红章, 杨德林, 胡婕, 郝好山, 胡行

郑州大学物理工程学院, 郑州大学材料物理教育部重点实验室, 郑州 450052

收稿日期:2004-12-13 修回日期:2005-02-23 出版日期:2006-01-20 网络出版日期:2006-01-20

Oxygen Permeability of Mixed Ionic and Electronic Conductivity Y_1-xLa_xBa₂Cu₃O_7-δ Membranes

SONG Hong-Zhang, YANG De-Lin, HU Jie, HAO Hao-Shan, HU Xing

School of Physical Engineering, Material Physics Key Laboratory of Ministry of Education, Zhengzhou University, Zhengzhou 450052, China

Received:2004-12-13 Revised:2005-02-23 Published:2006-01-20 Online:2006-01-20

摘要/Abstract

摘要： 用稳态法研究了具有类钙钛矿结构的Y_1-xLa_xBa₂Cu₃O_7-δ(x=0.1、0.3、0.5、0.8和1.0) 致密透氧膜在750～1000℃之间的透氧量. 实验发现, 透氧速率随着La替
代Y的比例x的增加而增加; 在大约875℃, 氧空位的有序-无序转变导致透氧率有一个突然增加. 透氧膜的两侧分别为He气氛和空气, 当La完全替代Y时, 厚1.0mm的LaBa₂Cu₃O_7-δ
膜的透氧量达到1.22μmol/s·cm²(1.64 mL/min·cm²).

关键词: 类钙钛矿, 透氧膜, Y_1-xLa_xBa₂Cu₃O_7-δ, 透氧率

Abstract: Oxygen permeation fluxes through dense perovskite-related type Y_1-xLa_xBa₂Cu₃O_7-δ(x=0.1, 0.3, 0.5, 0.8 and 1.0) membranes were investigated by the steady state permeation method in a temperature
range from 750℃ to 1000℃. Oxygen permeation flux increases with the increase in La element substitution proportions, and increases sharply at about 875℃ due to an order-
disorder transition of the oxygen vacancies in the membrane. oxygen flux of LaBa₂Cu₃O_7-δ(x=1.0) membrane with thickness 1.0mm reaches 1.22 μmol/s·cm² (1.64 mL/min·cm²)
under air/He gradients at 1000℃.

Key words: perovskite-related type, oxygen permeation membrane, Y_1-xLa_xBa₂Cu₃O_7-δ, oxygen flux

中图分类号:

O484

宋红章,杨德林,胡婕,郝好山,胡行. 混合导电体Y_1-xLa_xBa₂Cu₃O_7-δ透氧膜的透氧性能研究[J]. 无机材料学报.

SONG Hong-Zhang,YANG De-Lin,HU Jie,HAO Hao-Shan,HU Xing. Oxygen Permeability of Mixed Ionic and Electronic Conductivity Y_1-xLa_xBa₂Cu₃O_7-δ Membranes[J]. Journal of Inorganic Materials.

参考文献

[1] Teraoka Y, Zhang H M, Furukawa S, et al. Chem. Lett., 1985. 1743-1746.
[2] Steele B C H. Solid State Ionics, 1995, 75: 157-165.
[3] 周午纵, 梁维耀.《高温超导基础研究》. 上海: 上海科技出版社, 1999. 33-35.
[4] 高之爽, 杨德林, 王振峰, 等. 2002年材料科学与工程新进展. 北京: 冶金工业出版社, 2003. 300-312.
[5] Hu Xing, Zhu Zhili, Guo Lanjing, et al. Sensors and Actuators B, 2004, 99: 310.
[6] Yang Delin, Lu Hongxia, Song Hongzhang, et al. J. Membr. Sci., 2004, 233: 45-50.
[7] Chen C S, Ran S, Liu W, et al. Angew. Chem. Int. Ed, 2001, 40: 784-786.
[8] Tong Jianhua, Yang Weishen, Zhu Baichun, et al. J. Membr. Sci., 2002, 203: 175-189.
[9] Shao Zhongping, Yang Weishen, Cong You, et al. J. Membr. Sci., 2000, 172: 177-188.
[10] 樊传刚, 刘卫, 江国顺 (FAN Chuan-Gang, et al). 无机材料学报(Journal of Inorganic Materials), 2004, 19 (1): 121-126.
[11] Skakle J M S. Materials Sciences and Engineering, 1998, R23: 1-40.
[12] Chen Chu-sheng, Zhang Zhan-ping, Jiang Guo-sun, et al. Chem. Mater., 2001, 13: 2797-2800.
[13] Aasland S, Tangen I L, Wiik K, et al. Solid State Ionics, 2000, 135: 713-717.
[14] Kilner J A, Brook R J. Solid State Ionics, 1982, 6: 237-252.
[15] Kruidhof H, Bouwmeester H J M, Doorn R H E, et at. Solid State Ionics, 1993, 63-65: 816-822.
[16] Zeng Y, Lin Y S, Swartz S L. J. Membr. Sci., 1998, 150: 87-98.
[17] 宋红章, 杨德林, 卢红霞, 等.《低温与超导》, 2003, 31 (4): 34-38.
[18] Cook R L, Macduff R C, Sammells A F. J. Electrochem. Soc., 1990, 137: 3309-3310.
[19] Cook R L, Sammells A F. Solid State Ionics, 1991, 45: 311-321.
[20] Kilner J A, De Souza R A, Fullarton I C. Solid State Ionics, 1996, 86-88: 703-709.

混合导电体Y_1-xLa_xBa₂Cu₃O_7-δ透氧膜的透氧性能研究

Oxygen Permeability of Mixed Ionic and Electronic Conductivity Y_1-xLa_xBa₂Cu₃O_7-δ Membranes

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 10

编辑推荐

Metrics

本文评价

[1]	刘雪娇, 何振宇, 吴昊, 骆婷, 孟夑, 陈初升, 占忠亮. 浸渍LaNi_0.6Fe_0.4O_3-_δ纳米颗粒对Zr_0.84Y_0.16O_2-_δ- La_0.8Sr_0.2Cr_0.5Fe_0.5O_3-_δ透氧膜性能的影响[J]. 无机材料学报, 2018, 33(1): 14-18.
[2]	张莉莉, 李可, 于称称, 张玉文, 吴成章, 丁伟中. Ag-Cu钎料与双相陶瓷透氧膜的润湿和界面反应研究[J]. 无机材料学报, 2016, 31(6): 607-612.
[3]	刘林, 方有维, 邓新峰, 庄文东, 唐斌, 张树人. (Ba_1-xSr_x)La₄Ti₄O₁₅(x=0.8~0.95)陶瓷的微结构及微波介电性能研究[J]. 无机材料学报, 2012, 27(3): 281-284.
[4]	王芳, 梁春生, 徐大亮, 曹慧群, 孙宏元, 罗仲宽. 锂空气电池的研究进展[J]. 无机材料学报, 2012, 27(12): 1233-1242.
[5]	申梓刚，路朋献，胡行. 利用激光刻蚀技术提高Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3-δ膜的透氧能力[J]. 无机材料学报, 2010, 15(2): 221-224.
[6]	谭小耀,孟波,杨乃涛. 陶瓷中空纤维透氧膜的制备与性能[J]. 无机材料学报, 2006, 21(1): 245-249.
[7]	杨小毛,罗来涛,钟华. LaSrCoO₄催化材料的制备及性能的研究[J]. 无机材料学报, 2005, 20(2): 413-418.
[8]	樊传刚,刘卫,江国顺,宋春林,陈初升. La_0.2Ba_0.8(Co_0.2Fe_0.8)_1-xZr_xO_3-δ透氧膜材料的微结构与氧分离性能研究[J]. 无机材料学报, 2004, 19(1): 121-126.
[9]	张华,金江,余桂郁,杨南如,施剑林,冯景伟. La₂NiO_4+δ透氧膜材料的结构特点与性能[J]. 无机材料学报, 2001, 16(3): 440-446.
[10]	刘卫,章占平,夏长荣,谢津桥,陈初升. 多孔La_0.6Sr_0.4Co_0.2Fe_0.8O_3-δ的制备及表征[J]. 无机材料学报, 2000, 15(5): 849-854.