表面择优取向析晶β-BaB2O3透明玻璃陶瓷的研究

无机材料学报

表面择优取向析晶β-BaB₂O₃透明玻璃陶瓷的研究

张勤远; 姜中宏; 胡丽丽

中国科学院上海光学精密机械研究所; 上海201800

收稿日期:1996-02-29 修回日期:1996-03-22 出版日期:1997-06-20 网络出版日期:1997-06-20

A Study on GrAlN-Oriented Transparent β-Barium Borate Crystallized Glass Ceramics

ZHANG Qinyuan; JIANG Zhonghong; HU Lili

Shanghai Institute of Optics Fine Mechanics; Chinese Academy of SciencesShanghai 201800 China

Received:1996-02-29 Revised:1996-03-22 Published:1997-06-20 Online:1997-06-20

摘要/Abstract

摘要： 本文采用传统熔融方法制备了BaO－B₂O₃系列基础玻璃（BaO－B₂O₃、BaO-B₂O₃-0.1Al₂O₃、BaO－B₂O₃－0.2SiO₂、BaO－B₂O₃－0．4TiO₂）（mol％），通过对基础玻璃进行表面修饰处理，控制表面析晶条件，获得了含有沿α轴择优取向生长BBO微晶的透明BaO-B₂O₃系列表面析晶玻璃陶瓷．

关键词: 玻璃表面, 微晶玻璃陶瓷, 玻璃析晶

Abstract: Optically transparent BaO-B₂O₃ (in mol%) system glass was successfully prepared by theconventional melting and quenching technique. After surface controlled crystallization, the grAlN-oriented transparent β-BaB₂O₃ (BBO) surface crystallized glass -ceramics were prepared. Inaddition, the polar-oriented growth kinetics of BaO-B₂O₃ glass was discussed.

Key words: glass surface, submicrometer glass-ceramics, glass crystallization

张勤远,姜中宏,胡丽丽. 表面择优取向析晶β-BaB₂O₃透明玻璃陶瓷的研究[J]. 无机材料学报.

ZHANG Qinyuan,JIANG Zhonghong,HU Lili. A Study on GrAlN-Oriented Transparent β-Barium Borate Crystallized Glass Ceramics[J]. Journal of Inorganic Materials.

[1]	张海军,姚熹,张良莹,吴明忠. Ba₂Zn_ZCo_2-ZFe₁₂O₂₂-SiO_₂微晶玻璃陶瓷的sol-gel合成及性能研究[J]. 无机材料学报, 2003, 18(4): 759-764.
[2]	张海军,姚熹,张良莹. BaFe₁₂O₁₉/SiO₂微晶玻璃陶瓷的柠檬酸盐Sol-Gel合成及其微波性能的研究[J]. 无机材料学报, 2001, 16(6): 1069-1076.
[3]	张勤远,姜中宏,胡丽丽. 透明BaO·B₂O₃玻璃陶瓷的表面形貌、结构特征及光学性能[J]. 无机材料学报, 1997, 12(4): 482-486.

表面择优取向析晶β-BaB₂O₃透明玻璃陶瓷的研究

A Study on GrAlN-Oriented Transparent β-Barium Borate Crystallized Glass Ceramics

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 3

编辑推荐

Metrics

本文评价