溶液pH对液相沉积氢氧化镍薄膜的影响

王汝娜, 李群艳, 王志宏, 韦奇, 聂祚仁   

  1. 北京工业大学材料科学与工程学院, 北京 100022
  • 收稿日期:2006-09-25 修回日期:2006-11-28 出版日期:2007-09-20 网络出版日期:2007-09-20

Influence of Solution pH on Nickel Hydroxide Thin Films Prepared by Liquid Phase Deposition

WANG Ru-Na, LI Qun-Yan, WANG Zhi-Hong, WEI Qi, NIE Zuo-Ren   

  1. College of Materials Science and Engineering, Beijing University of Technology, Beijing 100022, China
  • Received:2006-09-25 Revised:2006-11-28 Published:2007-09-20 Online:2007-09-20

PDF (PC)

1712

被引次数

18

摘要： 采用液相沉积法在不同pH值溶液中制备了多孔氢氧化镍(Ni(OH)2)薄膜. 当溶液pH值在7.5～8.8之间变化时, 能在基片上形成均匀连续的由Ni(OH)2纳米棒搭接组成的多孔薄膜, 主要晶型为β-Ni(OH)2. 溶液pH值的微小变化会引起薄膜中棒状Ni(OH)2尺寸的显著改变: 当pH=7.5时, Ni(OH)2纳米棒的长度约为80nm, 直径约为50nm; 当pH=7.8时, Ni(OH)2纳米棒的长度增大到180nm, 直径约为60nm; 当pH=8.0时, Ni(OH)2纳米棒的长度显著增大约为300nm, 直径约为70nm. 然而, 当pH=8.3时, Ni(OH)2纳米棒的长度减小约为230nm, 直径约为80nm; 当pH=8.8时, 纳米棒长度迅速减小约为110nm, 直径减小约为55nm. 结合Ni(OH)2成核、生长过程和β-Ni(OH)2晶体结构特点讨论了溶液pH值对Ni(OH)2薄膜微观形态的影响机制.

关键词: 氢氧化镍, 液相沉积, 多孔薄膜

Abstract: Nickel hydroxide (Ni(OH)2) thin films were deposited from a variety of solutions with different pH values by liquid phase deposition. Continuous Ni(OH)2 thin films were obtained within the pH ranging from 7.5 to 8.8. The nucleation and growth process of Ni(OH)2, and β-Ni(OH)2 crystallization were used to discuss the influence of solution pH on the microstructures of the Ni(OH)2 films. The thin films are made of Ni(OH)2 nanorods mainly with β-Ni(OH)2 crystallinity and there are a lot of open pores between the nanorods in the Ni(OH)2 films. The dimensions of Ni(OH)2 nanorods change remarkably with the pH of reactive solutions. When solution’s pH is 7.5, the length of nanorods is about 80nm and the diameter is about 50nm. When solution’s pH increases to 7.8, the length of nanorods increases to about 180nm and the diameter is about 60nm. When solution’s pH increases to 8.0, the length of nanorods sharply increases to about 300nm and the diameter is about 70nm. However, when solution’s pH increases to 8.3, the length of nanorods decreases to about 230nm and the diameter is about 80nm. When solution’s pH increases to 8.8, the length of nanorods sharply decreases to about 110nm and the diameter is about 55nm.

Key words: nickel hydroxide, liquid phase deposition, porous thin films