流延成型结合反应熔渗制备ZrB2-SiC陶瓷及其微观结构与氧化行为研究
谭敏1,2(
), 陈小武1,2(), 杨金山1,2, 张翔宇1,2, 阚艳梅1,2, 周海军1,2, 薛玉冬1,2, 董绍明1,2()
), 陈小武1,2(), 杨金山1,2, 张翔宇1,2, 阚艳梅1,2, 周海军1,2, 薛玉冬1,2, 董绍明1,2()
Microstructure and Oxidation Behavior of ZrB2-SiC Ceramics Fabricated by Tape Casting and Reactive Melt Infiltration
TAN Min1,2(), CHEN Xiaowu1,2(), YANG Jinshan1,2, ZHANG Xiangyu1,2, KAN Yanmei1,2, ZHOU Haijun1,2, XUE Yudong1,2, DONG Shaoming1,2()
), CHEN Xiaowu1,2(), YANG Jinshan1,2, ZHANG Xiangyu1,2, KAN Yanmei1,2, ZHOU Haijun1,2, XUE Yudong1,2, DONG Shaoming1,2()
.
Fig. 10. Thickness of the oxide layer of ceramics oxidized at 1600 ℃ for different periods