三元层状材料结构调控及性能研究进展

丁浩明, 李勉, 李友兵, 陈科, 肖昱琨, 周洁, 陶泉争, 尹航, 柏跃磊, 张毕堃, 孙志梅, 王俊杰, 张一鸣, 黄振莺, 张培根, 孙正明, 韩美康, 赵双, 王晨旭, 黄庆

Progress in Structural Tailoring and Properties of Ternary Layered Ceramics

DING Haoming, LI Mian, LI Youbing, CHEN Ke, XIAO Yukun, ZHOU Jie, TAO Quanzheng, Johanna Rosen, YIN Hang, BAI Yuelei, ZHANG Bikun, SUN Zhimei, WANG Junjie, ZHANG Yiming, HUANG Zhenying, ZHANG Peigen, SUN Zhengming, HAN Meikang, ZHAO Shuang, WANG Chenxu, HUANG Qing

表3 部分MAB相的理论体积模量(B)、剪切模量(G)、杨氏模量(E)和泊松比(ν)

Table 3 Theoretical mechanical properties of several MAB-phases, including bulk modulus (B), shear modulus (G), Young’s modulus (E), and Poisson ratio (ν)

MAB phase B/GPa G/GPa E/GPa ¯ν/GPa Ref. Mn2AlB2 239 169 411 0.21 [160] Fe2AlB2 209 133 329 0.24 Co2AlB2 216 92 242 0.31 TiAlB 145 116 274 0.18 VAlB 173 133 317 0.19 NbAlB 180 130 315 0.21 TaAlB 192 138 333 0.21 CrAlB 189 140 338 0.20 MnAlB 167 101 252 0.25 TcAlB 220 114 292 0.28 Sc2AlB2 238 142 356 0.25 Ti2AlB2 170 150 347 0.16 Zr2AlB2 152 112 270 0.20 Hf2AlB2 168 132 314 0.19 V2AlB2 195 129 317 0.23 Nb2AlB2 199 110 279 0.27 Cr2AlB2 229 177 422 0.19 Mo2AlB2 238 142 356 0.25 W2AlB2 262 139 354 0.28 Tc2AlB2 260 132 339 0.28 Ni2AlB2 200 91 237 0.30 MoAlB 213 146 357 0.22 [164] WAlB 232 146 362 0.24 Mn2AlB2 222 161 388 0.21 [165] Fe2AlB2 210 132 329 0.24 [165] Co2AlB2 241 101 266 0.31 [166] Zr3CdB4 — 82 202 0.37 [167] Hf3PB4 — 180 407 0.19 [168]