Cansas-II SiCf/SiC复合材料的高温拉伸蠕变行为
Tensile Creep Behavior of Cansas-II SiCf/SiC Composites at High Temperatures
(a) As-received; (b) Crept at 1200 ℃/110 MPa for 560 h; (c) Crept at 1200 ℃/120 MPa; (d) Crept at 1200 ℃/140 MPa
Cansas-II SiCf/SiC复合材料的高温拉伸蠕变行为 |
| 荆开开, 管皞阳, 朱思雨, 张超, 刘永胜, 王波, 王晶, 李玫, 张程煜 |
|
Tensile Creep Behavior of Cansas-II SiCf/SiC Composites at High Temperatures |
| JING Kaikai, GUAN Haoyang, ZHU Siyu, ZHANG Chao, LIU Yongsheng, WANG Bo, WANG Jing, LI Mei, ZHANG Chengyu |
| 图4 2D-SiCf/SiC在不同条件下的断口宏观形貌 |
| Fig. 4 Macroscopic morphologies of fractures of 2D-SiCf/SiC under different conditions (a) As-received; (b) Crept at 1200 ℃/110 MPa for 560 h; (c) Crept at 1200 ℃/120 MPa; (d) Crept at 1200 ℃/140 MPa |
|
|