聚碳硅烷基复合涂层PCS裂解行为及其抗激光烧蚀性能
蔡佳1,2(
), 赵芳霞1(), 范栋1,2, 黄利平2, 牛亚然2(), 郑学斌2, 张振忠1
), 赵芳霞1(), 范栋1,2, 黄利平2, 牛亚然2(), 郑学斌2, 张振忠1
Pyrolysis Behavior and Laser Ablation Resistance of PCS in Polycarbosilane Composite Coatings
CAI Jia1,2(), ZHAO Fangxia1(), FAN Dong1,2, HUANG Liping2, NIU Yaran2(), ZHENG Xuebin2, ZHANG Zhenzhong1
), ZHAO Fangxia1(), FAN Dong1,2, HUANG Liping2, NIU Yaran2(), ZHENG Xuebin2, ZHANG Zhenzhong1
图11. YSZ、YPT和YPY涂层经2123和4246 W/cm2激光分别烧蚀5和10 s的(a)表面形貌和(b)背面形貌
Fig. 11. Surface morphologies (a) and back surface morphologies (b) of YSZ, YPT and YPY coatings ablated by 2123 and 4246 W/cm2 laser for 5 and 10 s, respectively