Pyrolysis Behavior and Laser Ablation Resistance of PCS in Polycarbosilane Composite Coatings
CAI Jia1,2(), ZHAO Fangxia1(), FAN Dong1,2, HUANG Liping2, NIU Yaran2(), ZHENG Xuebin2, ZHANG Zhenzhong1
), ZHAO Fangxia1(), FAN Dong1,2, HUANG Liping2, NIU Yaran2(), ZHENG Xuebin2, ZHANG Zhenzhong1
图10. YPT和YPY原始涂层(a, d)和经425 W/cm2激光烧蚀5 s的SEM截面形貌(b, c, e, f)及EDS结果(g, h)
Fig. 10. Cross-sectional original SEM morphologies (a, d), cross-sectional morphologies (b, c, e, f) and EDS results (g, h) of YPT and YPY coatings after 425 W/cm2, 5 s laser ablation