无机酸铝体系氧化铝连续纤维的制备技术研究
贾玉娜1(
), 曹旭2, 焦秀玲1, 陈代荣1()
), 曹旭2, 焦秀玲1, 陈代荣1()
Preparation of Alumina Ceramic Continuous Fibers with Inorganic Acidic Aluminum Sol as Precursor
JIA Yuna1(), CAO Xu2, JIAO Xiuling1, CHEN Dairong1()
), CAO Xu2, JIAO Xiuling1, CHEN Dairong1()
图S1. 氧化铝陶瓷连续纤维经不同温度热处理后的SEM照片(全貌(1)、表面(2)、截面(3))
Fig. S1. SEM images of alumina ceramic continuous fiber after heat-treatment at different temperatures (overview (a1-e1), surface (a2-e2), cross section (a3-e3))
(a) 1000 ℃/1 h; (b) 1100 ℃/1 h; (c) 1200 ℃/1 h; (d) 1300 ℃/0.5 h; (e) 1400 ℃/0.5 h