微波加热制备特种陶瓷材料研究进展
陈勇强1(
), 王怡雪1, 张帆1,2, 李红霞1,3, 董宾宾4, 闵志宇4, 张锐1,4()
), 王怡雪1, 张帆1,2, 李红霞1,3, 董宾宾4, 闵志宇4, 张锐1,4()
Preparation of Special Ceramics by Microwave Heating: a Review
CHEN Yongqiang1(), WANG Yixue1, ZHANG Fan1,2, LI Hongxia1,3, DONG Binbin4, MIN Zhiyu4, ZHANG Rui1,4()
), WANG Yixue1, ZHANG Fan1,2, LI Hongxia1,3, DONG Binbin4, MIN Zhiyu4, ZHANG Rui1,4()
图10. 不同摩尔分数La2O3掺杂ZTA陶瓷的SEM照片[
Fig. 10. SEM images of ZTA ceramics doped with different molar contents of La2O3[
(a-d) Microwave sintering at 1550℃ for 30 min at La2O3 content of (a) 0, (b) 1.5%, (c) 3%, and (d) 5%; (e) Conventional sintering at 1600℃ for 3 h at La2O3 content of 1.5%