Research Progress on Ultrahigh Temperature Oxide Eutectic Ceramics by Laser Additive Manufacturing
LIU Haifang1,2(), SU Haijun1,2(), SHEN Zhonglin1, JIANG Hao1, ZHAO Di1, LIU Yuan1, ZHANG Jun1, LIU Lin1, FU Hengzhi1
), SU Haijun1,2(), SHEN Zhonglin1, JIANG Hao1, ZHAO Di1, LIU Yuan1, ZHANG Jun1, LIU Lin1, FU Hengzhi1
图11. LDED制备的Al2O3/YAG共晶陶瓷各相在熔池凝固过程中的生长方向演变[
Fig. 11. Orientation variations of eutectic phases of the LDED-processed Al2O3/YAG eutectic ceramic during solidification process[
(a) EBSD orientation maps of Al2O3 and YAG in bottom zone of the molten pool; (b) Orientation variations of Al2O3 and YAG along the height direction of the molten pool