闪烧合成高熵氧化物陶瓷(MgCoNiCuZn)O的性能
李汪国1(
), 刘佃光1(), 王珂玮2, 马百胜2, 刘金铃3
), 刘佃光1(), 王珂玮2, 马百胜2, 刘金铃3
High Entropy Oxide Ceramics (MgCoNiCuZn)O: Flash Sintering Synthesis and Properties
LI Wangguo1(), LIU Dianguang1(), WANG Kewei2, MA Baisheng2, LIU Jinling3
), LIU Dianguang1(), WANG Kewei2, MA Baisheng2, LIU Jinling3
图3. 不同电流密度闪烧样品以及相应温度传统烧结样品微观结构对比
Fig. 3. Comparison of microstructures of flash sintered samples with different current densities and conventional sintered samples at corresponding temperatures
(a-e) Microstructures of flash sintered samples; (f-j) Microstructures of conventional sintered samples