Preparation and High Temperature Inorganic Transformation of Flexible Silicone Aerogels
LUO Yi1(), XIA Shuhai2, NIU Bo2, ZHANG Yayun2, LONG Donghui2()
), XIA Shuhai2, NIU Bo2, ZHANG Yayun2, LONG Donghui2()
图3. 样品V/VM-3在空气氛围下的TG-IR谱图(a, b), 经不同温度处理后的实物图(c)和在800 ℃处理后的SEM照片(d)
Fig. 3. (a, b) TG-IR spectra of sample V/VM-3 tested in air; (c) Photographs of sample V/VM-3 after heat-treated at different temperatures; (d) SEM image of sample V/VM-3 after heat-treated at 800 ℃