锂离子电池高镍LiNi0.8Mn0.2O2正极材料的微波合成及其Co、Al共改性
|
|
付宇坤, 曾敏, 饶先发, 钟盛文, 张慧娟, 姚文俐
|
Microwave-assisted Synthesis and Co, Al Co-modification of Ni-rich LiNi0.8Mn0.2O2 Materials for Li-ion Battery Electrode
|
|
FU Yukun, ZENG Min, RAO Xianfa, ZHONG Shengwen, ZHANG Huijuan, YAO Wenli
|
|
表S2 材料在不同倍率下的放电比容量
|
Table S2 Specific discharge capacities of materials at different rates/(mAh·g-1)
|
|
| Sample | 0.2C | 0.5C | 1C | 2C | 3C | 4C | 5C | 0.2C | | NM-82 | 195.57 | 183.52 | 175.03 | 164.59 | 157.33 | 149.26 | 141.49 | 185.66 | | NMCA-0 | 192.45 | 182.66 | 176.69 | 166.91 | 160.88 | 157.05 | 153.17 | 183.80 | | NMCA-1 | 189.79 | 182.60 | 177.43 | 169.72 | 165.24 | 162.25 | 158.83 | 187.36 | | NMCA-2 | 189.70 | 183.05 | 177.84 | 172.80 | 169.08 | 164.76 | 160.03 | 189.25 | | NMCA-3 | 187.28 | 180.32 | 174.85 | 168.60 | 162.63 | 158.61 | 156.14 | 187.50 | | NMCA-5 | 186.04 | 178.28 | 173.83 | 167.08 | 163.41 | 157.97 | 150.84 | 181.33 |
|
|
|