La(Co0.2Cr0.2Fe0.2Mn0.2Ni0.2)O3钙钛矿高熵陶瓷粉体的制备及其电学性能
郭猛(
), 张丰年, 苗洋(), 刘宇峰, 郁军, 高峰
), 张丰年, 苗洋(), 刘宇峰, 郁军, 高峰
Preparation and Electrical Properties of High Entropy La(Co0.2Cr0.2Fe0.2Mn0.2Ni0.2)O3 Perovskite Ceramics Powder
GUO Meng(), ZHANG Fengnian, MIAO Yang(), LIU Yufeng, YU Jun, GAO Feng
), ZHANG Fengnian, MIAO Yang(), LIU Yufeng, YU Jun, GAO Feng
图4. 800 ℃煅烧La(Co0.2Cr0.2Fe0.2Mn0.2Ni0.2)O3样品的SEM照片(a), 1000 ℃煅烧La(Co0.2Cr0.2Fe0.2Mn0.2Ni0.2)O3样品的SEM照片(b)及其元素的EDS分布(c~g)
Fig. 4. SEM image of sample La(Co0.2Cr0.2Fe0.2Mn0.2Ni0.2)O3 calcined at 800 ℃ (a), SEM image (b) and corresponding EDS element mapping (c-g) of La(Co0.2Cr0.2Fe0.2Mn0.2Ni0.2)O3 calcined at 1000 ℃