钙钛矿型(La0.2Li0.2Ba0.2Sr0.2Ca0.2)TiO3高熵氧化物陶瓷的制备及性能研究
张晓燕1,2,3(
), 刘馨玥1,2, 闫金华1,2, 谷耀行1,2, 齐西伟3,4()
), 刘馨玥1,2, 闫金华1,2, 谷耀行1,2, 齐西伟3,4()
Preparation and Property of High Entropy (La0.2Li0.2Ba0.2Sr0.2Ca0.2)TiO3 Perovskite Ceramics
ZHANG Xiaoyan1,2,3(), LIU Xinyue1,2, YAN Jinhua1,2, GU Yaohang1,2, QI Xiwei3,4()
), LIU Xinyue1,2, YAN Jinhua1,2, GU Yaohang1,2, QI Xiwei3,4()
图3. 不同温度烧结(La0.2Li0.2Ba0.2Sr0.2Ca0.2)TiO3高熵陶瓷的SEM照片
Fig. 3. SEM images of high entropy (La0.2Li0.2Ba0.2Sr0.2Ca0.2)TiO3 ceramic sintered at different temperatures
(a) 1250 ℃; (b) 1300 ℃; (c) 1350 ℃; (d)1400 ℃; (e) 1450 ℃; (f) 1500 ℃