单相双稀土改性SrZrO3热障涂层的热物理性能
马伯乐1,2,马文1,2(
),黄威1,2,白玉1,2,贾瑞灵1,2,董红英2,3
),黄威1,2,白玉1,2,贾瑞灵1,2,董红英2,3
Thermophysical Property of Single-phase Strontium Zirconate Co-doped with Double Rare-earth Oxides as a Thermal Barrier Coating Material
Bo-Le MA1,2,Wen MA1,2(),Wei HUANG1,2,Yu BAI1,2,Rui-Ling JIA1,2,Hong-Ying DONG2,3
),Wei HUANG1,2,Yu BAI1,2,Rui-Ling JIA1,2,Hong-Ying DONG2,3
图8. 涂层火焰循环测试后的(a~b)宏观形貌和(c~d)截面显微形貌
Fig. 8. Photographs (a-b) and SEM microstructures (c-d) of coatings after burner rig tests
(a, c) Sr1.1(Zr0.9Yb0.05Gd0.05)O3.05; (b, d) Sr1.1(Zr0.9Yb0.05Gd0.05)O3.05/YSZ