Thermophysical Property of Single-phase Strontium Zirconate Co-doped with Double Rare-earth Oxides as a Thermal Barrier Coating Material
Bo-Le MA1,2,Wen MA1,2(),Wei HUANG1,2,Yu BAI1,2,Rui-Ling JIA1,2,Hong-Ying DONG2,3
),Wei HUANG1,2,Yu BAI1,2,Rui-Ling JIA1,2,Hong-Ying DONG2,3
图3. 1600 ℃热处理不同时间涂层的热膨胀曲线
(a) Sr1.1(Zr0.9Yb0.05Gd0.05)O3.05; (b) SrZrO3
Fig. 3. TECs of two different coatings after heat-treatment at 1600 ℃ for different time