| 表2 Ti3C2Tx、Ti3C2Tx/PVA和PVA薄膜物理性质[53] |
| Table2 Physical properties of Ti3C2Tx, Ti3C2Tx/PVA and PVA films[53] |
|
| MXene content/wt% | Thickness/μm | Conductivity/(S·m-1) | Tensile strength/MPa | Young’s modulus/GPa | Strain to failure/% | | 100 | 3.3 | 240238±3500 | 22±2 | 3.52±0.01 | 1.0±0.2 | | 90 | 3.9 | 22433±1400 | 30±3 | 3.00±0.01 | 1.8±0.3 | | 80 | 6.1 | 137±3 | 25±4 | 1.7±0.2 | 2.0±0.4 | | 60 | 7.2 | 1.30±0.08 | 43±8 | 1.8±0.6 | 3.0±0.5 | | 40 | 12.0 | 0.040±0.003 | 91±10 | 3.70±0.02 | 4.0±0.5 | | 0 | 13.0 | - | 30±5 | 1.0±0.3 | 15.0±6.5 |
|
|
|