膜/块体结构氧化物复合磁电材料研究进展
王婧1, 吴霞2, 邓朝勇2, 朱孔军1, 南策文3

Research Progress of Film/Bulk Oxide Magnetoelectric Composites
WANG Jing1, WU Xia2, DENG Chao-Yong2, ZHU Kong-Jun1, NAN Ce-Wen3
图4 MPB-PZTAgCFO, PZT-PZNAgCFO和商用PZTAgCFO磁电耦合系数随外加偏置直流磁场的变化关系, 插图为CFO的d E d H 和|d #cod#x003bb; 11 d H |随磁场的变化关系 [ 20 ]
Fig. 4 Magnetoelectric voltage coefficient of MPB-PZTAgCFO, PZT-PZNAgCFO and PZTAgCFO as a function of applied magnetic bias. The inset shows d E d H and |d #cod#x003bb; 11 d H | with applied magnetic field [ 20 ]