彭犇1,2, 邱桂博1, 岳昌盛1, 张梅1, 郭敏1

Controllable Synthesis of One-dimensional β-SiAlON Materials
PENG Ben1,2, QIU Gui-Bo1, YUE Chang-Sheng1, ZHANG Mei1, GUO Ming1
图5 #cod#x003b2;-SiAlON材料XRD特征峰 I 210 I 200 衍射强度比值随生长温度的变化
Fig. 5 Ratio of #cod#x003b2;-SiAlON XRD characteristic diffraction peaks intensity I 210 and I 200 vs growth temperature