聚合物热解法制备碳纳米管/铝复合粉末及其反应动力学研究
徐润1, 李忻达1, 李志强1, 赵仁宇1, 范根莲1, 熊定邦1, 唐婕1, 许勇2, 张荻1

Preparation and Reaction Kinetics of Carbon Nanotubes/Aluminum Composite Powders Using Polymer Pyrolysis Method
XU Run1, LI Xin-Da1, LI Zhi-Qiang1, ZHAO Ren-Yu1, FAN Gen-Lian1, XIONG Ding-Bang1, TANG Jie1, XU Yong2, ZHANG Di1
图6 在873 K反应a0 min、b30 min、c60 min后CNTs的SEM形貌和长度分布以及d不同反应时间CNTsAl复合粉末的拉曼光谱
Fig.6 SEM images with length and normalized frequency statistic inset of the CNTs after grown at 873 K for a 0 min, b 30 min and c 60 min. d Raman spectra of the CNTAl composite powders The lengths of CNTs were measured on the corresponding SEM images randomly, and 120 CNTs were counted at each reaction time