剧烈-温和阳极氧化结合法快速制备有序阳极氧化铝膜的研究

郝爱文^1,², 黄丽清¹, 程龙¹, 李新¹, 张薇薇¹, 单冬至¹, 冯雪红¹

Fast Fabrication of Highly Ordered Porous Anodic Alumina Membranes by Hard-mild Anodization

HAO Ai-Wen^1,², HUANG Li-Qing¹, CHENG Long¹, Li Xin¹, ZHANG Wei-Wei¹, SHAN Dong-Zhi¹, FENG Xue-Hong¹

图3 U HO 为80 V时不同氧化时间所制备硫酸HA膜下表面的SEM照片插图为FFT图
Fig. 3 SEM images of PAA bottom surface fabricated by HA in 0.3 molL H 2 SO 4 -1.5℃ at U H = 80 VI Inset shows the FFT image of corresponding membrane a SEM image of PAA fabricated at t H = 25 min; b SEM image of PAA fabricated at t H = 20 min; c SEM image of PAA fabricated at t H =15 min; d SEM image of PAA fabricated at t H =10 min