具有SAF结构的IrMn基自旋阀材料的磁场退火研究
李健平1,2, 钱正洪1,2, 孙宇澄1,2, 白茹2, 刘建林2, 朱建国1

Effect of Magnetic Annealing on IrMn Based Spin Valve Materials with SAF Structure
Li Jian-Ping1,2, QIAN Zheng-Hong1,2, SUN Yu-Cheng1,2, BAI Ru2, LIU Jian-Lin2, ZHU Jian-Guo1
图2 退火前自旋阀材料样品的磁电阻曲线
Fig. 2 MR curves of the spin valve material before annealing