具有SAF结构的IrMn基自旋阀材料的磁场退火研究
李健平1,2, 钱正洪1,2, 孙宇澄1,2, 白茹2, 刘建林2, 朱建国1

Effect of Magnetic Annealing on IrMn Based Spin Valve Materials with SAF Structure
Li Jian-Ping1,2, QIAN Zheng-Hong1,2, SUN Yu-Cheng1,2, BAI Ru2, LIU Jian-Lin2, ZHU Jian-Guo1
图1 实验制备的自旋阀材料微观结构表征
Fig. 1 Characterization on microstructure of the as-deposited spin valve materials a Cross-section TEM image; b Surface AFM image