陶瓷/石墨烯块体复合材料的研究进展
李建林1, 陈彬彬1, 章文1, 王连军2, 江莞2

Recent Progress in Ceramic/Graphene Bulk Composites
LI Jian-Lin1, CHEN Bin-Bin1, ZHANG Wen1, WANG Lian-Jun2, JIANG Wan2
图2 球磨后的粉体FESEM照片
Fig. 2 FESEM micrographs of high energy ball milled graphite powder a As-milled graphite powder; b Graphite layers with a thickness of 20-50 nm that were highly distorted due to heavy impact of milling balls; c and d Carbon tubes with a diameter of 80-300 nm and a length of several microns produced during the milling [ 15 ]