新型复合支撑体共烧制备致密La0.7Ca0.3Cr0.97O3-δ连接体薄膜
王松林1,2, 凤仪2, 王东生1, 孟广耀3

Fabrication of Dense La0.7Ca0.3Cr0.97O3-δ Interconnect Membrane on Novel SOFC Composite Support by Co-firing
WANG Song-Lin1,2, FENG Yi2, WANG Dong-Sheng1, MENG Guang-Yao3
图5 不同NiO含量的NiOLCC97复合材料的热膨胀曲线
Fig. 5 Thermal expansion curves of NiOLCC97 composites with different NiO contents